Orthophthalic Polyester Resins
UPR 920
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 600 - 700 - Gel Time (min) 1,5% MEKP: -
UPR 925VI
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 250 - 350 - Gel Time (min) 1,5% MEKP: 60/90/120
UPR 930
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 500 - 600 - Gel Time (min) 1,5% MEKP: -
UPR 900TA
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800 - Gel Time (min) 1,5% MEKP: 15-25
UPR 900TAP
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800 - Gel Time (min) 1,5% MEKP: 10-20
UPR 900TAL
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800 - Gel Time (min) 1,5% MEKP: 15-25
UPR 900TAF
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 800 - 900 - Gel Time (min) 1,5% MEKP: 15-25
UPR 4650
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 800 - 900 - Gel Time (min) 1,5% MEKP: -
UPR 955B
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 800 - 900 - Gel Time (min) 1,5% MEKP: -
UPR 950S
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 500 - 700 - Gel Time (min) 1,5% MEKP: -
UPR 980HP
-
Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 500 - 600 - Gel Time (min) 1,5% MEKP: 15-20