High-Quality Unsaturated Polyester Resins

UPR 920

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 600 - 700
Gel Time (min) 1,5% MEKP: -

Description

orthophthalic, non-thixotropic, non-accelerated

Application

Castings

UPR 925VI

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 250 - 350
Gel Time (min) 1,5% MEKP: 60/90/120

Description

orthophthalic, non-thixotropic, pre-accelerated

Application

Vacuum Infusion

UPR 930

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 500 - 600
Gel Time (min) 1,5% MEKP: -

Description

orthophthalic, non-thixotropic, non-accelerated

Application

Pultrusion

UPR 900TA

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800
Gel Time (min) 1,5% MEKP: 15-25

Description

orthophthalic, non-thixotropic, pre-accelerated

Application

Marine and Transportation industry, Tanks, Containers, Pipes, etc (Lloyd's approval)

UPR 900TAP

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800
Gel Time (min) 1,5% MEKP: 10-20

Description

orthophthalic, non-thixotropic, pre-accelerated,promoted

Application

General purpose - Fast curing (Lloyd's approval)

UPR 900TAL

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800
Gel Time (min) 1,5% MEKP: 15-25

Description

orthophthalic, thixotropic, pre-accelerated, low styrene emission

Application

Marine and Transportation industry, Tanks, Containers, Pipes, etc (Lloyd's approval)

UPR 900TAF

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 800 - 900
Gel Time (min) 1,5% MEKP: 15-25

Description

orthophthalic, thixotropic, pre-accelerated, fire retardant

Application

Applications requiring a fire retardant resin (Rescue Boats, etc)

UPR 4650

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 800 - 900
Gel Time (min) 1,5% MEKP: -

Description

orthophthalic, non-thixotropic, non-accelerated, transparent

Application

Castings, statues, synthetic marbles

UPR 955B

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 800 - 900
Gel Time (min) 1,5% MEKP: -

Description

orthophthalic, non-thixotropic, non-accelerated

Application

Buttons

UPR 950S

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 500 - 700
Gel Time (min) 1,5% MEKP: -

Description

orthophthalic, non-thixotropic, non-accelerated

Application

Sanitary

UPR 980HP

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 500 - 600
Gel Time (min) 1,5% MEKP: 15-20

Description

orthophthalic, non-thixotropic, accelerated

Application

Hot Press

UPR IS 970

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 800 - 900
Gel Time (min) 1,5% MEKP: -

Description

Isohophthalic, non-thixotropic, non-accelerated

Application

Castings

UPR IS 975VI

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 250 - 350
Gel Time (min) 1,5% MEKP: 60/90/120

Description

Isohophthalic, non-thixotropic, pre-accelerated

Application

Vacuum Infusion

UPR IS 970TA

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800
Gel Time (min) 1,5% MEKP: 15-25

Description

Isohophthalic, thixotropic, pre-accelerated

Application

Marine and Transportation industry, Tanks, Containers, Pipes, etc (Lloyd's approval)

UPR 970TAP

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800
Gel Time (min) 1,5% MEKP: 10-20

Description

Isophthophthalic, thixotropic, pre-accelerated, promoted

Application

General purpose - fast curing (Lloyd's approval)

UPR 970TAL

Viscosity (mPa·s)
25˚C, sp2 - 20rpm: 700 - 800
Gel Time (min) 1,5% MEKP: 15-25

Description

Isophthophthalic, thixotropic, pre-accelerated, low styrene emission

Application

Marine and Transportation industry, Tanks, Containers, Pipes, etc (Lloyd's approval)